Structural and FT-IR Spectroscopic Studies of Mg-Cu-Zn Ferrite Nanoparticles Useful For Multilayer Chip Inductor
Keywords:
XRD, FTIR, Ferrites, NanoparticlesAbstract
Nanoparticles of MgxCu0.1Zn0.9-xFe2O4 (x = 0.5, 0.6, 0.7 ) ferrite have been preparaed by co-precipitation method at annealing temperature 600 oC. The results obtained from XRD and IR analysis are reported. XRD patterns confirm the formation of cubic spinel phase of ferrite samples along with secondary phase of ?-Fe2O3 with low concentration. The observed crystallite sizes are in the range of 20-24nm and the lattice parameter decreased with increase in Mg2+ ion concentration. FTIR spectra of three compositions gives only higher vibrational frequencies and no peaks of lower vibrational frequencies. This is due to presence of fine particles in the samples. The variation in ?1 shows that Cu is going to the octahedral site in Mg-Zn matrix. This paper reports the structural results obtained from XRD and FTIR studies and successed to densified ferrite powder at low sintering temperature useful for Multilayer Chip Inductros.
References
- A. Gabal, S. Kosa and T. S. Al Mutairi, J. Molecular Structure 1063, 269-273 (2014).
- I.Z. Rahman and T.T. Ahmed, J.Magn. Magn. Mate. 290-291, 1576-1579(2005).
- Ch. Srinivas, B.V. Tirupanyam, A. Satish, V. Sashubai, D. L. Sastry and O. F. Catun, J. Magn. Magn. Mater. 382, 15-19 (2015).
- A.S.Dzunuzovic, N.I.Ilic, M.M.Vijatovic Petrovic, J.D.Bobic, B.Stojadinovic, Z. Dohcevic-Mitrovic and B.D.Stojanovic, J. Magn. Magn. Mater. 374, 245-251 (2015).
- P.P.Naik, R.B.Tangasali, B.Sonaye and S.Sugur, J. Magn. Magn. Mater. 385, 377-385 (2015).
- A.Manikandan, J.Judith Vijaya, M.Sundararajan, C.Meganathan, L.John Kennedy and M.Bououdina, Superlattices and Microstructures, 64, 118-131 (2013).
- H.Anwar and A.Maqsood, J.Supercond.Nov.Magn 25, 1913-1920 (2012).
- V. D. Kapse, S. A. Ghosh, F. C. Raghuwamshi, S. D. Kapse and U. S. Khandekar, Talanta78, 19-25(2009).
- Muhammed Tan, Yuksel Koseoglu, Futkan Alan and Erdogan Senturk, J. Alloys and Compounds 509, 9399-9405 (2011).
- A. T. Raghavender, N. Biliskov and? Z. Skoko, Materials Letters 65, 677-680(2011)
Downloads
Published
Issue
Section
License
Copyright (c) IJSRST
This work is licensed under a Creative Commons Attribution 4.0 International License.