Thermoluminescence Properties of β-Ray Irradiated CaZnF4:Dy Phosphor

Authors

  • Tushar R. Shelke  Department of Physics, K.D.K. College of Engineering, Nagpur, Maharashtra, India
  • Govind B. Nair  Department of Physics, R.T.M. Nagpur University, Nagpur, Maharashtra, India
  • Vibha Chopra  P.G. Department of Physics & Electronics, DAV College, Amritsar, Punjab,India
  • N. S. Dhoble  Department of Chemistry, Sevadal Mahila Mahavidyalaya, Nagpur, Maharashtra, India
  • S. J. Dhoble  Department of Physics, R.T.M. Nagpur University, Nagpur, Maharashtra, India

Keywords:

Photoluminescence (PL); thermoluminescence (TL); beta-rays; wet chemical synthesis; fluoride.

Abstract

In this paper, thermoluminescence studies of CaZnF4: Dy phosphor, irradiated with beta-rays, has been reported. A series of CaZnF4: Dy phosphors were prepared by the wet chemical method and characterized for photoluminescence (PL) and Thermoluminescence (TL) properties. Under the photoluminescence study, the characteristic emission spectrum of Dy3+ corresponding to 4F9/2 → 6H15/2 (483 nm) and 4F9/2 → 6H13/2 (576 nm) transitions were observed. The Thermoluminescence (TL) glow curves of the prepared sample showed two well-defined glow peaks at 103 °C and 162 °C, respectively, indicating that two sets of traps is being activated within the particular temperature range. The trapping parameters associated with the prominent glow peak of CaZnF4: Dy was calculated by using Chen’s method.

References

  1. M.Y.A. Yagoub, H.C. Swart, E. Coetsee, J. Lumin. 187 (2017) 96-101.
  2. P. Molina, M. Santiago, J. Marcazzó, F. Spano, N. Khaidukov, E. Caselli, Radiat. Meas. 46 (2011) 1361-1364.
  3. E. Sullivan, T. Vogt, ECS J. Solid State Sci. Technol. 2 (2012) R3088-R3099.
  4. M. Que, Z. Ci, Y. Wang, G. Zhu, S. Xin, Y. Shi, Q. Wang, CrystEngComm 15 (2013) 6389.
  5. S. Tamboli, R.M. Kadam, S.J. Dhoble, Luminescence 31 (2016) 1321-1328.
  6. C. Feldmann, T. Jüstel, C.R. Ronda, P.J. Schmidt, Adv. Funct. Mater. 13 (2003) 511-516.
  7. W. Bin Im, S. Brinkley, J. Hu, A. Mikhailovsky, S.P. Denbaars, R. Seshadri, Chem. Mater. 22 (2010) 2842-2849.
  8. P.D. Belsare, C.P. Joshi, S. V. Moharil, S.K. Omanwar, P.L. Muthal, S.M. Dhopte, J. Lumin. 129 (2009) 135-139.
  9. P.D. Belsare, C.P. Joshi, S. V. Moharil, S.K. Omanwar, P.L. Muthal, S.M. Dhopte, Opt. Mater. 31 (2009) 668-672.
  10. P.D. Bhoyar, G.B. Nair, S.J. Dhoble, Opt.-Int. J. Light Electron Opt. 134 (2017) 33-44.
  11. S. Tamboli, S.J. Dhoble, Spectrochim. Acta Part A Mol. Biomol. Spectrosc. 184 (2017) 119-127.
  12. G.B. Nair, S.J. Dhoble, J. Fluoresc. 27 (2017) 575-585.
  13. G.B. Nair, S.J. Dhoble, RSC Adv. 5 (2015) 49235-49247.
  14. R. Chen, J. Appl. Phys. 40 (1969) 570-585.

International Journal of Scientific Research in Science and Technology

Downloads

Published

2018-01-30

Issue

Volume 4, Issue 1, January-February-2018

Section

Research Articles

License

Copyright (c) IJSRST

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.

How to Cite

[1]
Tushar R. Shelke, Govind B. Nair, Vibha Chopra, N. S. Dhoble, S. J. Dhoble "Thermoluminescence Properties of β-Ray Irradiated CaZnF4:Dy Phosphor" International Journal of Scientific Research in Science and Technology(IJSRST), Online ISSN : 2395-602X, Print ISSN : 2395-6011,Volume 4, Issue 1, pp.324-328, January-February-2018.